1、脱模剂在高温模压成型工艺中的应用
1. Application of release agent in high temperature molding process
碳纤维脱模剂涂刷在碳纤维复合材料模具上，然后将碳纤维的预浸料放置于上下模具之间，闭合模具时再将模具放置于液压台上进行高温高压成型操作，使树脂固化后，再取下碳纤维制品。这种成型技术具有高效、产品质量好、精度高等优点，适用于强度高、批量生产的复合材料产品的成型。
The carbon fiber release agent is applied on the carbon fiber composite mold, and then the carbon fiber prepreg is placed between the upper and lower mold. When the mold is closed, the mold is placed on the hydraulic table for high temperature and high pressure molding operation, so that the resin is solidified, and then the carbon fiber products are removed. This forming technology has the advantages of high efficiency, good product quality and high precision. It is suitable for the forming of composite products with high strength and mass production.
2、脱模剂在手糊成型工艺中的应用
2. Application of release agent in hand lay up process
在模具表面涂抹脱模剂、喷上胶衣，将剪裁好的碳纤维预浸布铺在模具表面上，然后刷上树脂类的产品，达到所需要的一定厚度时，就进行成型固化，最后脱模处理。
Apply mold release agent on the surface of the mold, spray on the gel coat, lay the cut carbon fiber prepreg on the surface of the mold, then brush on the resin products, when the required thickness is reached, the molding and curing will be carried out, and finally the mold release treatment will be carried out.